RM-3011 BMI FILM ADHESIVE
RM-3011 BMI FILM ADHESIVE
Renegade Materials Corporation specializes in manufacturing composite materials for aerospace applications, focusing on lightweight, engineered prepregs, adhesives, and hybrid composite systems to enhance fuel efficiency in aircraft structures.
The RM-3011 is a high-temperature Bismaleimide (BMI) film adhesive supported by an E-glass carrier. It offers good tack, drape, and high-temperature performance up to 400°F, suitable for co-curing, co-bonding, or secondary bonding applications.
- Standard Weight: 0.06 ± 0.010 psf (293 ± 48 gsm)
- Volatiles: < 2 wt%
- Density: 1.23 g/cc
- Film Thickness: 0.009 – 0.010 inches at 0.06 psf (0.229 – 0.254 mm)
- Coefficient of Thermal Expansion (CTE): 67 ppm/°C
- Dry Tg (DSC): 410°F (310°C) Post Cured at 450°F (232°C)
- Color: Amber
- Shelf Life: 6 months from shipment if stored at 0 ± 10°F
- Affordable with low minimum buy
- 3-4 week lead-time if not in stock
- Standard and custom film weights available
- Out-of-autoclave cure option
- Co-curable with most BMI prepreg materials
- Suitable for metallic, composite, and honeycomb structural bonding
- Service temperature: 350-400°F
- Single Lap Shear on Aluminum: 2250 psi at 75°F, 2390 psi at 350°F
- Flatwise Tensile Strength: 310 psi at 350°F
- Dielectric Constant (Dk): 3.209 at 8.2 – 12.4 GHz
- Loss Tangent (Df): 0.0137 at 8.2 – 12.4 GHz
- Vacuum Bag Cure in an Oven: Ramp from RT to 260°F at 5°F/min, hold for 1 hour, ramp to 375°F at 5°F/min, hold for 6 hours, ramp to 450°F at 5°F/min, hold for 6 hours, cool to RT.
- Co-Cure with Bismaleimide Prepreg: Follow prepreg manufacturer's instructions.
Renegade Materials offers two BMI prepreg systems compatible with RM-3011: RM-3002 for autoclave cure and RM-3004 for out-of-autoclave cure applications. Contact the company for more details.
This document and any pricing are proprietary and confidential, not to be disclosed to third parties without written consent from Renegade Materials Corporation.
Catalog excerpts
PRODUCT DATA SHEET RM-3011 BMI FILM ADHESIVE FOR HIGH PERFORMANCE AEROSPACE APPLICATIONS Renegade Materials Corporation is a global leader in manufacturing composite materials for aerospace applications. We deliver light-weight, highly-engineered prepregs, adhesives and hybrid composite systems to enable maximum fuel efficiency in commercial and military aircraft structures. For pricing or additional information on Renegade Materials’ products, please call us at 937-350-5274 or visit our website at www.renegadematerials.com 3363 South Tech Boulevard Miamisburg, OH 45342 Tel: 937-350-5274 Fax: 937-350-5275
Open the catalog to page 1
RM-3011 Bismaleimide Film Adhesive RM-3011 high temperature film adhesive is a Bismaleimide (BMI) film, supported with an E-glass carrier. RM-3011 provides good tack and drape, handling, and high temperature performance up to 400oF in extreme environments. It is designed for applications requiring co-curing, co-bonding, or secondary bonding. Affordable with Low Minimum Buy. 3 - 4 Week Lead-Time if Not in Stock. Standard (0.06 psf) and Custom Film Weights Available. Out-of-Autoclave (Vacuum Bag Only) Cure Option. Co-Curable with Most Bismaleimide Prepreg Materials. Suitable for Metallic, Composite,...
Open the catalog to page 2
^iTypical Mechanical Properties for RM-3011 Bismaleimide Film Adhesive *FWT Panel was co-cured Out of Autoclave with BMI skins on 3 lbs. Nomex core. -Waveguide test coupons (X-band) were machined from a 12" x 12" x 8 ply panel of RM-3011 Supported Film Adhesive (0.06 psf). -Machined coupons were dried at 180°F for 4 hours prior to testing. “Seller makes no warranty regarding the accuracy of this information. Buyers should make their own evaluation to determine suitability of any product for their own intended purposes." 3363 South Tech Boulevard Miamisburg, OH 45342 Tel: 937-350-5274 Fax: 937-350-5275...
Open the catalog to page 3
RM-3011 Bismaleimide Film Adhesive Recommended Cure Cycle Vacuum Bag Cure in an Oven 1) 2) 3) 4) 5) 6) 7) Ramp from RT to 260oF (127°C) @ 5oF (3°C) per minute. Hold for 1 hour. Ramp to 375oF (190°C) @ 5oF (3°C) per minute. Hold for 6 hours. Ramp to 450oF (232°C) @ 5oF (3°C) per minute. Hold for 6 hours. Cool down to RT. Co-Cure with Bismaleimide Prepreg* Follow the recommended cure and post cure instructions provided by the prepreg manufacturer. *Renegade Materials offers two Bismaleimide prepreg systems, RM-3002 for autoclave cure applications and RM-3004, for out of autoclave cure applications....