RM-1010 POLYIMIDE FILM ADHES IVE
RM-1010 POLYIMIDE FILM ADHES IVE
RM-1010 is a high-performance polyimide film adhesive designed for aerospace applications. It is supported with an E-glass carrier and is compatible with high-temperature polyimide prepregs like RM-1100 and AFR-PE-4. The adhesive offers excellent tack, drape, and high-temperature performance.
Typical Properties
- Weight: 0.06 or 0.10 ± 0.010 PSF
- Volatiles: 18-22 wt%
- Cured Thickness: 5 – 7 mils
- Glass Transition Temperature (Tg): 700°F with post-cure
- Shelf Life: 12 months at 0°F
PRIME-1010 Polyimide Primer Solution
- Solids Content: 8-12 wt%
- Density: 7 lb/gallon
- Shelf Life: 12 months at 0°F
- Application: Spray or Brush
- Recommended Drying: 1 hr at 350°F
Product Features
- Standard widths: 12-inch or 24-inch
- Co-cures with RM-1100 Polyimide prepreg
- Supported with E-glass scrim cloth for easy handling
- Suitable for bonding metallic, non-metallic, and honeycomb structures
- Available in paste and primer forms
- No MDA or other known carcinogenic ingredients
Recommended Cure Instructions
- Cure: 5°F/minute to 675°F ±10°F, hold for 2 hours in autoclave at 10-15” Hg, 50-100 psia
- Post-cure: Free standing in air at 675°F for 2 hours
Performance Testing
- Single Lap Shear on Titanium (ASTM-D1002) at 75°F: 2500 psi
- Single Lap Shear on Composite (ASTM-D1002) at 75°F: 2800 psi
- Single Lap Shear on Composite (ASTM-D1002) at 500°F: 2600 psi
Disclaimer
The seller makes no warranty regarding the accuracy of this information. Buyers should evaluate the product's suitability for their intended purposes.
Catalog excerpts
RM-1010 POLYIMIDE FILM ADHESIVE FOR HIGH PERFORMANCE AEROSPACE APPLICATIONS
Open the catalog to page 1
RM-1010 is an addition-cure polyimide film, supported with an E-glass carrier. This product was formulated for use with the industry's highest service temperature polyimide prepregs, including RM-1100 and AFR-PE-4. RM-1010 adhesives provide excellent tack and drape, and out-time, and exhibit high-temperature performance in extreme environments. Standard width 12-inch or 24-inch RM-1010 Adhesive Film co-cures with RM-1100 Polyimide prepreg RM-1010 films are supported with E-glass scrim cloth for easy handling. Suitable for metallic, non-metallic, and honeycomb structure bonding Paste and Primer...
Open the catalog to page 2
Recommended Cure Instructions > Cure: 5°F/minute to 675°F +/-10°F. Hold 2-hours in autoclave 10-15" Hg, 50-100-psia. > Post-cure: Free standing, in air, 675°F for 2 hours Seller makes no warranty regarding the accuracy of this information. Buyers should make their own evaluation to determine suitability of any product for their own intended purposes." 3363 South Tech Boulevard Miamisburg, OH 45342 Tel: 937-350-5274 Fax: 937-350-5275 Page 2
Open the catalog to page 3
3363 South Tech Boulevard Miamisburg, OH 45342 Tel: 937-350-5274
Open the catalog to page 4All RENEGADE MATERIALS CORPORATION/MAVERICK CORPORATION catalogs and technical brochures
RM-3011 BMI FILM ADHESIVE4 Pages
MVK-10 Polyimide 101 Page