RM-1005 POLYIMIDE FILM ADHESIVE
RM-1005 POLYIMIDE FILM ADHESIVE
- Available in standard and custom film weights without extra cost.
- Offers a wide range of processing options, including low-temperature (350°F) cure and out-of-autoclave (vacuum bag only) cure.
- Co-curable with many polyimide prepreg materials.
- Suitable for bonding metallic, non-metallic, and honeycomb structures.
- No known carcinogenic materials, such as methylene dianiline (MDA).
- Service temperature can be tailored with specific cure and post-cure conditions.
- Single Lap Shear on Titanium: 2600 psi at 75°F, 2700 psi at 75°F (different conditions).
- Single Lap Shear on Composite: 2500 psi at 75°F, decreasing to 925 psi at 650°F.
- Flat-Wise Tension: 650 psi at 75°F, 250 psi at 600°F.
- Cure conditions involve heating to 350°F for 2 hours, followed by a free-standing post-cure at 600°F for 2 hours.
- Different cure conditions apply for autoclave and oven processes.
- Shelf life of 6 months at 0°F.
- Volatile content ranges from 22-28 wt%.
- Dry glass transition temperature (Tg) is 620°F, dependent on cure and post-cure conditions.
Catalog excerpts
RM-1005 POLYIMIDE FILM ADHESIVE FOR HIGH PERFORMANCE AEROSPACE APPLICATIONS
Open the catalog to page 1
RM-1005 Polyimide Film Adhesive RM-1005 high temperature adhesive is a condensation-cure polyimide film, supported with an E-glass carrier. RM-1005 provides good tack and drape, handling, and high temperature performance in extreme environments. Also available as a paste (RM-1005-PASTE) and a primer (PRIME-1005) Affordable with No Minimum Buy or Set-Up Charges 2 – 3 Week Lead-Time Standard and Custom Film Weights Available at no extra cost Wide range of processing options including low-temp (350°F) cure Out-of-Autoclave (vacuum bag only) cure option Co-Curable with many polyimide prepreg materials...
Open the catalog to page 2
MATERIALS CORPORATION “Seller makes no warranty regarding the accuracy of this information. Buyers should make their own evaluation to determine suitability of any product for their own intended purposes." 3363 South Tech Boulevard Miamisburg, OH 45342 Tel: 937-350-5274 Fax: 937-350-5275 Page 2
Open the catalog to page 3
Notes for Mechanical Property Table 1 - Cure conditions: 4°F(2.22°C)/min to 350°F (177°C) for 2 hours in autoclave with 15 in Hg (381 mm Hg) and 35 psi (0.24 MPa). Free standing post cure 600°F (316°C) for 2 hours 2 - Cure conditions: 4°F(2.22°C)/min to 350°F (177°C)for 2 hours in oven with full vacuum. Free standing post cure 600°F (316°C)for 2 hours 3 - AFR-PE-4 Polyimide-graphite composite laminates 4 - AFR-PE-4 Polyimide/T650-35 Carbon fabric laminates with 1/2” (1.3 cm) HRH327 polyimide honeycomb core, 3/16” (0.5 cm) cell size, 4.5 lb (2.0 kg) density “Seller makes no warranty regarding...
Open the catalog to page 4
Renegade Materials Corporation is a global leader in manufacturing composite materials for aerospace applications. We deliver light-weight, highly-engineered prepregs, adhesives and hybrid composite systems to enable maximum fuel efficiency in commercial and military aircraft structures. For pricing or additional information on Renegade products, please call us at 937-350-5274 or visit our website at www.renegadematerials.com This document and any pricing provided on this product are considered proprietary, confidential and competition-sensitive and are not to be disclosed to any third parties...