PRIMER P60-LC
1 / 4Pages

PRIMER P60-LC COATINGS FOR AIRCRAFT STRUCTURE PROTECTION Product information Water-reducible epoxy primer three components containing low amount of Strontium chromate. This product is designed for the protection of metallic structures on Aircraft. Base P 60-LC Hardener / Catalyst P 60-A Thinner Demineralised water Qualified in accordance with: Airbus: A2MS 565-001 Gr B Cat 1&2, Ty I Bombardier: BAMS 565-001 Grade B Category 1, Type I & Category 2, Type I DHMS C 4.01 Type 2 Product information mentioned in the technical datasheet is given for information purposes and can differ from requirements of specifications above. In that case, customer requirements are valid for your application. Physical properties THEORETICAL COVERAGE 37 m²/l (1500 ft²/gal) for 15 µm (0.6 mils) dry (base and not diluted hardener) DRY FILM WEIGHT 1.7 VOC 160 g/l (ISO11890-1) and 340 g/l (ASTM D3960) COLOR Green SHELF LIFE / STORAGE 18 months for the base and hardener, stored between 5°C and 35°C (41°F and 95°F) in full and sealed original packaging. 12 months in Touch-Up Kits, stored between 5°C and 35°C (41°F and 95°F) in full and sealed original packaging. GLOSS LEVEL 20 GU below 60° NOTES Gloss levels have been determined using glossmeter with an angle of incidence of 60°C. The theorical consumption value doesn’t take into account the transfer efficiency for spray application Surface preparation P60-LC primer is used particularly on aluminium alloys that have had the following treatments: Alodine 1200: Cr6 conversion CAA: Chromic Acid Anodising SAA: Sulphuric Acid Anodising TSA: Tartaric Sulphuric Anodising BAA: Boric Acid Anodising Observe the recoating time between the surface treatment and painting. This may vary depending on the treatment and industrial instructions. Contact us for information on uses on other metallic structures, surface treatments or paints. P60-LC primer can also be used on sealants. All recommandations mentioned above are given for information. Technical Data Sheet N° 25 - Edition (01/2020)

PRIMER P60-LC COATINGS FOR AIRCRAFT STRUCTURE PROTECTION SPRAY APPLICATION MIXING RATIO Mixing ratio by weight 100 38 65 to 130 Base Hardener / Catalyst Water Mixing ratio by volume 2V 1V 2 V to 4V MIXING PROCEDURE Ideally, the unmixed products should be stored between 18°C and 25°C (64°F and 77°F) for 24 hours before use. The P60-LC base should be mixed for 10 minutes in a pneumatic or oscillating mixer before use. When using 200L drums, we recommend tumbling the drums on a roller or tumbler for 2 to 4 hours prior to placing under the impeller system, then an initial stirring at about 200...

PRIMER P60-LC COATINGS FOR AIRCRAFT STRUCTURE PROTECTION BRUSH APPLICATION Base Hardener / Catalyst Water Mixing ratio by weight Mixing ratio by volume 100 2V 38 1V 0 or 35 to 50 0 V or 1 V to 1.5 V MIXING PROCEDURE Remove the safety ring and press down on the cap to release the P60-A hardener. Shake the container for approximately 1 minute. Remove the cap to be able to apply the P60-LC primer with a suitable brush. If the material after shaking 1min is not homogenious please use a stick for futher mixing (around 1min) util the material is homogen. When diluting fill the hardener capsulte...

PRIMER P60-LC COATINGS FOR AIRCRAFT STRUCTURE PROTECTION Drying times Dust free Not Applicable 5 minutes 15 minutes 10 minutes Dry to handle 35 minutes 15 minutes 1 hour 45 30 minutes 25 minutes Dry to tape minutes 1 hour 30 minutes 25 minutes 15 minutes Dry to sand 8 hours to 45 minutes to 30 minutes to 1 5 to 35 Recoatable 48 hours 1 hour 45 hour 30 minutes minutes minutes 3 days 2 hours 1hour 45 35 minutes Fully Cured minutes NOTE Drying times have been determined using test pieces of a thickness < 2 mm and for 15 µm (0.6 mils) of dry film. Before accelerated drying ≥ 70°C, leave to...