PRIMER P60-2K
4Pages

PRIMER P60-2K COATINGS FOR AIRCRAFT STRUCTURE PROTECTION Product information Strontium chromate-based, two component water-reducible epoxy primer, with high chemical resistance. This product is designed for the protection of metallic structures on aircraft. P60-2K primer is recommended for use in combination with Mapaero F70-2K structural topcoat. Base P60-2K Hardener / Catalyst H2K Qualified to: Embraer: MEP 10-059 Type III Product information mentioned in the technical datasheet is given for information purposes and can differ from requirements of specifications above. In that case, customer requirements are valid for your application. Physical properties THEORETICAL COVERAGE 18 m²/l (800 ft²/gal) for 15 µm (0.6 mils) dry DRY FILM WEIGHT 1.7 VOC 160 g/l (ISO11890-1) and 340 g/l (ASTM D3960) COLOR Green SHELF LIFE / STORAGE 12 months for the base and hardener, sstored between 5°C and 35°C (41°F and 95°F) in full and sealed original packaging. 12 months in P60-A Touch-Up Kits, stored between 5°C and 35°C (41°F and 95°F) in full and sealed original packaging. GLOSS LEVEL 20 GU below 60° NOTES Gloss levels have been determined using glossmeter with an angle of incidence of 60°C. The theorical consumption value doesn’t take into account the transfer efficiency for spray application Surface preparation P60-2K primer is used particularly on aluminium alloys that have had the following treatments: Alodine 1200: Cr6 conversion CAA: Chromic Acid Anodising SAA: Sulphuric Acid Anodising TSA: Tartaric Sulphuric Anodising BAA: Boric Acid Anodising Observe the recoating time between the surface treatment and painting. This may vary depending on the treatment and industrial instructions. Contact us for information on uses on other metallic structures, surface treatments or paints. P60-2K primer can also be used on sealants. All recommandations mentioned above are given for information. Technical Data Sheet N° 31 - Edition (02/2020)

PRIMER P60-2K COATINGS FOR AIRCRAFT STRUCTURE PROTECTION SPRAY APPLICATION MIXING RATIO Base Hardener / Catalyst Mixing ratio by weight 100 18 Mixing ratio by volume 5V 1V MIXING PROCEDURE Ideally, the unmixed products should be stored between 18°C and 25°C (64°F and 77°F) for 24 hours before use. The P60-2K base should be mixed for 10 minutes in a pneumatic or oscillating mixer before use. Mix the base and hardener until the mixture is homogenous. The mixture must be made at a temperature between 15°C and 35°C (60°F and 95 °F). Sieve the paint through a 120-150 µm (4.0-6.0 mils) filter....

PRIMER P60-2K COATINGS FOR AIRCRAFT STRUCTURE PROTECTION BRUSH APPLICATION Base Hardener / Catalyst Mixing ratio by weight Mixing ratio by volume 100 2V 38 1V MIXING PROCEDURE Remove the safety ring and press down on the cap to release the hardener. Shake the container for approximately 1 minute. Remove the cap to be able to apply the P60-2K primer with a suitable brush. If yhe material after shaking 1min is not homogenious, please use a stick for futher mixing (around 1min) until the material is homogen. Do not hermetically close TUKs after mixing base and hardener. POT LIFE 4 hours at...

PRIMER P60-2K COATINGS FOR AIRCRAFT STRUCTURE PROTECTION Drying times Dust free Recoatable Fully Cured 60°C (140°F) N.A* 30 minutes to 2 hours 3 hours NOTE Drying times have been determined using test pieces of a thickness < 2 mm and for 15 µm (0.6 mils) of dry film. Before accelerated drying ≥ 70°C, leave to flash off for at least 15 minutes at room temperature. Before recoating the P60-2K with the F70-2K finish, drying is recommended at 60°C (140°F) or more. To recoat P60-2K primer with another product, contact us. For the infrared drying of P60-2K primer, contact us. *N.A. : Not...