Applications Springs, Fasteners, Washers, Zippers, Clips, Clamps, Computer Parts, Contacts, Stampings of a wide variety of parts, Pins. Description Type 301 is an austenitic stainless steel capable of attaining high strengths and ductility by cold working. It is not hardenable by heat treatment. Type 301 is non-magnetic in the annealed condition and becomes increasingly magnetic with cold working. It is preferable over types 302 and 304 in the tempered condition because the higher enlongations (which are attainable at a given strength level) facilitate fabrication. Chemistry Typical Carbon: 0.15 max Manganese: 2.00 max Silicon: 1.00 max Chromium: 16.00-18.00 Nickel: 6.00- 8.00 Aluminum: 0.75 max Phosphorus: 0.040 max Sulphur: 0.030 max Copper: 0.75 max Nitrogen: 0.10 max Iron: Balance Physical Properties Density: 0.285 lbs/in3 7.88 g/cm3 Electrical Resistivity: microhm-in (microhm-cm): 68 °F (20 °C): 27.4 (69.5) Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels & Special Metals, Inc., be liable for any damages arising from the use of the Information Included In this document or that It Is suitable for the 'applications' noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document. Copyright January 2014 Revision 06.20.2017. Ulbrich Stainless Steels & Special Metals, Inc. All rights reserved. We Deliver Precision®

 Open the catalogue to page 1

Specific Heat: BTU/lb/°F (kJ/kg-K): 32-212 °F (0-100 °C): 0.12 (0.50) Thermal Conductivity: BTU/hr/ft2/ft/°F (W/nvK) At 212 °F (100 °C)-9.4 (16.2), At 932 °F (500 °C) - 12.4 (21.4) Mean Coefficient of Thermal Expansion: in/in/°F (pm/nvK) 32-212 °F (0-100 °C) - 9.4 x 10'6 (16.9) 32 - 600 °F (0-315 °C) - 9.9 x 10 6 (17.8) 32 - 1000 °F (0 - 538 °C) - 10.2 x 10 6 (18.4) 32 - 1200 °F (0 - 649 °C) - 10.4 x 10 6 (18.7) Modulus of Elasticity: ksi (MPa) In tension: 28.0 x 103 (193 x 103) In torsion: 11.2 x 103 (78 x 103) Magnetic Permeability: H = 200 Oersteds: Annealed < 1.02 max. Melting Range: 2250...

 Open the catalogue to page 2

1/4 Hard Ultimate Tensile Strength: 125 KSI min (860 MPA) Yield Strength: (0.2% Offset) 75 KSI min/515 MPA min Elongation: 25% Min 1/2 Hard Ultimate Tensile Strength: 150 KSI min (1035 MPA min) Yield Strength: (0.2% Offset) 110 KSI min (760 MPA min) Elongation: 15%<.015" 18%>.015" 3/4 Hard Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength: (0.2% Offset) 135 KSI MIN/515 MPA MIN Elongation: 10%< .015" 12%> .015" Full Hard Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength: (0.2% Offset) 140 KSI min (965 MPA min) Elongation: 8% < .015" 9%> .015" Extra Full Hard Ultimate...

 Open the catalogue to page 3

301 STAINLESS STEEL Additional Properties Corrosion Resistance 301 has good corrosion resistance and is used in many food service applications, similar to grade 304. Finishes # 1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a smooth decorative finish is not required. # 2D - Dull finish produced by cold rolling, annealing and descaling. Used for deep drawn parts and those parts that need to retain lubricants in the forming process. # 2B - Smooth finish produced by cold rolling, annealing and descaling. A light cold rolling pass...

 Open the catalogue to page 4

All Ulbrich catalogues and technical brochures

  1. Corporate Brochure

    16 Pages

    En
  2. 302

    3 Pages

    En
  3. 301SI

    3 Pages

    En
  4. 204CU

    4 Pages

    En
  5. 201

    3 Pages

    En