Applications Springs, Fasteners, Utensils, Food Service, Appliances, Automotive Trim, Clamps Description Type 201 stainless steel is an austenitic chromium-nickel-manganese stainless alloy. It was developed mid century to conserve nickel and it is used as an alternative to type 301 in some tempered applications. Because of 201’s relatively high yield strength in the annealed condition, use of 201 is limited. Type 201 is generally used in the tempered condition particularly for springs and fasteners. 201 Stainless will retain a comparable ductility to 301 even with the higher yield strength. Chemistry Typical Carbon: 0.15 max Manganese: 5.50- 7.50 max Phosphorus: 0.060 max Sulfur: 0.030 max Silicon: 0.75 max Chromium: 18.00- 20.00 max Nickel: 3.50- 5.50 Nitrogen: 0.25 max Iron: Balance Physical Properties Density: 0.283 lbs/in3 7.81 g/cm3 Electrical Resistivity: microhm-in, (microhm-cm): 27.0 (68.5) Specific Heat: BTU/lbs./°F (kJ/kg/K): 32-212 °F (0-100 °C): 0.12 (0.50) Thermal Conductivity, BTU/hr/ft/ft2/°F (W/m/K): At 212 °F (100 °C): 9.4(16.2) At 932 °F (500 °C): 12.4 (21.4) Limitation of Liability and Disclaimer of Warranty: In no event will Ulbrich Stainless Steels & Special Metals, Inc., be liable for any damages arising from the use of the Information Included In this document or that It Is suitable for the 'applications' noted. We believe the information and data provided to be accurate to the best of our knowledge but, all data is considered typical values only. It is intended for reference and general information and not recommended for specification, design or engineering purposes. Ulbrich assumes no implied or express warranty in regard to the creation or accuracy of the data provided in this document. Copyright January 2014 Revision 06.01.2015. Ulbrich Stainless Steels & Special Metals, Inc. All rights reserved. We Deliver Precision®

 Open the catalog to page 1

Modulus of Elasticity, ksi (MPa) 28.6 x 103 (197 xIO3) Magnetic Permeability, H=200 Oersteds: Annealed < 1.02 max Melting Range: 2550 - 2650 °F (1399 -1454 °C) Forms Coil - Strip, Foil, Ribbon Wire - Profile, Round, Flat, Square Mechanical Properties at Room Temperature Annealed Condition Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 38 KSI min (260 MPA min) Elongation: 40%min Hardness: B95 max Tempered 1/16 Hard Ultimate Tensile Strength: 95 KSI min (655 MPA min) Yield Strength (0.2% Offset): 45 KSI min (310 MPA min) Elongation: 40% min Tempered 1/8...

 Open the catalog to page 2

Tempered 3/4 Hard Ultimate Tensile Strength: 175 KSI min (1205 MPA min) Yield Strength (0.2% Offset): 135 KSI min (930 MPA min) Elongation: 10% < 0.15” 12% > 0.15” Tempered Full Hard Ultimate Tensile Strength: 185 KSI min (1275 MPA min) Yield Strength (0.2% Offset): 140 KSI min (965 MPA min) Elongation: 8% < 0.15” 9% > 0.15” Additional Properties Corrosion Resistance Refer to NACE (National Associate of Corrosion Engineers) for recommendations. Finishes for Strip & Foil #1 - Hot rolled annealed and descaled. It is available in strip, foil and ribbon. It is used for applications where a...

 Open the catalog to page 3

All Ulbrich catalogs and technical brochures

  1. 302

    3 Pages

  2. 301SI

    3 Pages

  3. 301

    4 Pages

  4. 204CU

    4 Pages